4B  American standard – ASTM  Rg7 (Cu Sn7 Zn4 Pb7), CC493K

8A  American standard – ASTM  CW710R (Cu Zn35 Ni3 Mn2 Al Pb, Sonderm.)

8C  American standard – ASTM  SS 5234 (Cu Zn25 Al 5, SoMsF75), CC762S

9D  American standard – ASTM  SS 5716-15 (Cu Al10 Ni5 Fe4 F70), AB-200

AB1  British standard / BS 1400  SS 5710-15 (Cu Al10 Fe3), CC331G

AB2  British standard / BS 1400  SS 5716-15 (Cu Al10 Ni5 Fe4 F70), AB-200

C102  British standard / BS 2872/2874  W340 (Cu Cr Zr), CW106C

C 112  British standard / BS 2872/2874  W210 (Cu Co2 Be), CW104C

CA 104  British standard / BS 2872/2874  SS 5716-20 (Cu Al10 Ni5 Fe4 F74), AB-220 Ni

CC1-TF  British standard / BS 1400  W340 (Cu Cr Zr), CW106C

CT 2  British standard / BS 1400  SS 5465 m. extra Nickel, CC484K

CZ114  British standard / High Tensile Brass (HTB)  CW713R (Cu Zn37 Mn3 Al2 Pb Si, Sonderm.)

HTB 1  British standard / High Tensile Brass (HTB)  ~CW710R (Cu Zn35 Ni3 Mn2 Al Pb, Sonderm.)

HTB 3  British standard / High Tensile Brass (HTB)  SS 5234 (Cu Zn25 Al 5, SoMsF75), CC762S

LB1  British standard / BS 1400  Cu Pb15 Sn (Cu Sn7 Pb15-C), CC496K

LB2  British standard / BS 1400  SS 5640-15 (Cu Pb10 S

两相黄铜（从H63至H59），合金组织中除了具有塑性良好的α相外，还出现了由电子化合物CuZn为基的β固溶体。β相在高温下具有很高的塑性，而低温下的β′相（有序固溶体）性质硬脆。故(α+β)黄铜应在热态下进行锻造。含锌量大于46%～50%的β黄铜因性能硬脆，不能进行压力加工。

力学性能

黄铜中由于含锌量不同，机械性能也不一样，黄铜的机械性能随含锌量不同而变化。对于α黄铜，随着含锌量的增多，σb和δ均不断增高。对于(α+β)黄铜，当含锌量增加到约为45%之前，室温强度不断提高。若再进一步增加含锌量，则由于合金组织中出现了脆性更大的r相（以Cu5Zn8化合物为基的固溶体），强度急剧降低。（α+β）黄铜的室温塑性则始终随含锌量的增加而降低。所以含锌量超过45%的铜锌合金无实用价值。

普通黄铜的用途很为广泛如水箱带、供排水管、奖章、波纹管、蛇形管、冷凝管、 壳及各种形状复杂的冲制品、小五金件等。随着锌含量的增加从H63到H59，它们均能很好地承受热态加工，多用于机械及电器的各种零件、冲压件及乐器等处。