NS 16544  Norwegian standard / NS  Cu Pb20 Sn 5, (Cu Sn5 Pb20-V), CC497K

NS 16550  Norwegian standard / NS  SS 5144 (Cu Zn33 Pb2), CC750S

NS 16554  Norwegian standard / NS  SS 5253 (Cu Zn39 Pb2 Al), CB754S, CC754S

NS 16565  Norwegian standard / NS  SS 5256 (Cu Zn35 Al1), ~CW710R  (CuZn35Ni2) 

NS 16570-15  Norwegian standard / NS  SS 5716-15 (Cu Al10 Ni5 Fe4 F70), AB-200

NS 16570-20  Norwegian standard / NS  SS 5716-20 (Cu Al10 Ni5 Fe4 F74), AB-220 Ni

LM’s comparison list between different

norms from Copper alloys

Please read below on the wished for trade-name in the left hand column, and get it translated into LM-language on the right-hand

column. The right hand column with our name is either identical in composition or a fully replaceable alloy with only minor

differences. The column in the middle states the norm and its country of origin.

With no marks in front of LM’s alloy = alloy is identical, with this sign “~” = alloy is very similar, fully replaceable.

QAL7：具有高的强度和 性，在大气、淡水、海水和某些酸中耐蚀性高，可热、冷态压力加工，可电焊和气焊，不易钎焊。

用途： 簧盒要求耐蚀的其它 性元件。

QAL9-4：具有高的强度，良好的减摩性和很好的耐蚀性，可热加工，可焊接，但不易钎焊。

用途：高强、耐磨零件，如轴承、轴套、齿轮、涡轮等；还可制造接管嘴、法兰盘、扁形摇臂、支架等。

QAL10-4-4：在400℃以下具有稳定的力学性能，有良好的减摩性，在大气、淡水、海水中耐蚀性很好，可热加工，可焊接，但不易钎焊。

用途：高强度的耐磨零件盒在400℃以下工作的零件，如轴承、轴套、齿轮、球形座、螺帽、法兰盘等。

主要分析方法：化学成分的影响

化学成分对铝青铜组织与性能的影响一直是关注的热点之一。首先，化学成分对合金作用的好与坏并没有一个明确的界定。如铁加入铝青铜中一般起到细化晶粒、减小“自发回火脆性”、提高力学性能的作用，但当铁含量较高时，铁会以Fe3Al2化合物析出，使合金的机械性能变坏，因此铁含量不应超过5%。还有锌元素，很多研究认为它与基体金属固溶后，可提高金属的塑性，而也有研究认为其为杂质元素。由此看出，合金元素的作用不能一概而论。普遍认为加入适量的合金元素可改善合金的机械性能，如加入适量的铁形成铝铁青铜，加入锰形成铝锰青铜，加入镍形成铝镍青铜。其次，对于杂质元素含量的要求还没有一个明确的界定。正是由于化学成分的变化才使得铝青铜的种类和应用场合各不相同，研究者应该不断研究化学成分的影响、作用机理，进一步扩大铝青铜的应用范围。

强化